Journal of Alloys and Compounds
Partial isothermal sections at 810 700 and 585 degrees C are presented for a high-Al compositional range of Al-Cu-Mo The maximal solubility of Cu in the Al(5)Mo phase(s) was found to be similar to 3 at % The previously reported Al(3)Ti-type phase was found to be formed around the Al(68) (5)Cu(6) (5)Mo(25) composition The other ternary phase forming in a small compositional range around Al(7)Cu(2)o has a hexagonal structure with a = 0 86796(8) and c = 1 51948(12)nm (C) 2010 Elsevier B V All rights reserved